NUCLEATE POOL BOILING FROM SELECTIVE LASER MELTED MICROGROOVES/ MICROCAVITIES SURFACES WITH HFE-7000

Jin Yao Ho
School of Mechanical and Aerospace Engineering Nanyang Technological University 50 Nanyang Avenue, Singapore 639798 Republic of Singapore

Kin Keong Wong
Singapore Centre for 3D Printing, School of Mechanical and Aerospace Engineering, Nanyang Technological University, 50 Nanyang Avenue, Singapore 639798, Republic of Singapore

Kai Choong Leong
Singapore Centre for 3D Printing, School of Mechanical and Aerospace Engineering, Nanyang Technological University, 50 Nanyang Avenue, Singapore 639798, Republic of Singapore

Charles Yang
School of Mechanical and Aerospace Engineering Nanyang Technological University 50 Nanyang Avenue, Singapore 639798 Republic of Singapore

DOI: 10.1615/TFESC1.mph.013076
pages 1917-1928


键词 Pool boiling, critical heat flux, selective laser melting, HFE-7000

摘要

Microscale surface modification techniques for enhancing nucleate pool boiling performance have shown significant progress in the last three decades. Selective laser melting (SLM), with the ability to fabricate highly complex and ordered structures, offers an alternative surface modification technique for promoting boiling. This technique utilizes a laser source which selectively melts and fuses the base metal powder in accordance to pre-programmed models in successive layers. With adequate control of the laser intensity and scanning positions, structured microscale surfaces can be produced.

In the present study, two 10 mm × 10 mm microstructured surfaces were fabricated using the SLM technique with AlSi10Mg metallic powder of 20 to 63 µm distribution size range. Surfaces 1 and 2 contain 500 µm and 700 µm sized microcavities, respectively. In addition, the microcavities were separated by microgrooves with average distances of 120 and 150 µm. Saturated pool boiling experiments were performed on these surfaces with HFE-7000 in a thermosyphon. The results show that the microstructured surfaces enhanced heat transfer by up to 30% as compared to a plain surface and critical heat flux as high as 50.5 W/cm2 was achieved. In addition, the microgrooves were observed to be active nucleation sites whereas the microcavities were found to be inactive sites. These observations agree well with the theoretical analysis performed, where the active cavities sizes were calculated to be between 0.05 and 164 µm. Finally, correlations are proposed to characterize the pool boiling curves of these surfaces taking into consideration the effects of their microfeatures.